TEHNICKE KARAKTERISTIKE TERMOPLAST MATERIJALA |
||||||||||
POSMATRANE OSOBINE |
Standard |
JED. MERE |
TERMOPLAST |
PA-11 |
TEKSTO- LIT |
TERMOPLAST |
||||
60 |
80Mo |
L |
PE |
PP |
PTFE |
|||||
MEHANICKE OSOBINE |
||||||||||
ZATEZNA CVRSTOCA |
– DIN 53455 |
N/mm2 |
80 |
80-85 |
80 |
67 |
22 |
32 |
20-35 |
|
+ DIN 53455 |
40 |
50-60 |
55 |
67 |
22 |
32 |
20-35 |
|||
ISTEZANJE KOD PREKIDA |
– DIN 53455 |
% |
110 |
30-50 |
300 |
80 |
20-35 |
Ca 450 |
Ca 650 |
200-400 |
+ DIN 53455 |
300 |
100 – 200 |
20-35 |
Ca 450 |
Ca 650 |
200-400 |
||||
MODUL ELAST. (ISTEZANJE) |
– ISTEZANJE |
N/mm2 |
2700 |
2900 |
900 |
0,7×104 |
3000 |
950 |
Ca 1200 |
750 |
+ ISTEZANJE |
1600 |
1800 |
2800 |
950 |
Ca 1200 |
750 |
||||
MODUL ELAST. (SAVIJANJE) |
– SAVOJNO |
N/mm2 |
2400 |
2600 |
790 |
|||||
+ SAVOJNO |
1200 |
1500 |
790 |
|||||||
GRANICNO SAVOJNO NAPREZANJE |
– DIN 53452 |
N/mm2 |
120 |
130 |
55 |
27 |
45 |
|||
+ DIN 53452 |
35 |
110 |
27 |
45 |
||||||
ŽILAVOST |
+ DIN 53453 |
KJ/m2 |
bez prekida |
80 |
4,3 |
30 |
bez prekida |
bez prekida |
||
DINAMICKA ŽILAVOST NA 20°C |
+ DIN 53453 |
KJ/m2 |
Ca 100 |
15 |
15-30 |
9-10 |
bez prekida |
4-8 |
||
DINAMICKA ŽILAVOST NA 0°C |
+ DIN 53453 |
KJ/m2 |
8,5-9,5 |
Ca 4 |
||||||
DINAMICKA ŽILAVOST NA -20°C |
+ DIN 53453 |
KJ/m2 |
8-9 |
Ca 2 |
||||||
DINAMICA ŽILAVOST NA -40°C |
+ DIN 53453 |
KJ/m2 |
7,5-8,5 |
|||||||
TVRDOCA |
– DIN 53505 |
SHORE D |
78 |
70 |
80-83 |
64-67 |
69 |
60 |
||
(SHORE D) |
+ DIN 53505 |
65 |
80-83 |
64-67 |
69 |
60 |
||||
FIZICKE OSOBINE |
||||||||||
GUSTINA |
DIN 53479 |
g/cm3 |
1,13 |
1,14 |
1,04 |
1,4 |
1,41 |
0,94 |
0,905 |
2,20 |
TEMPE RATURA TOPLJENJA |
DIN 53736 |
K |
Ca 488 |
Ca 528 |
458 |
Ca 400 |
Ca 438 |
408 |
Ca 433 |
600 |
SPECIFICNA TOPLOTA |
c |
J/kgK |
1674 |
1674 |
2428 |
2428 |
1464 |
1841 |
1925 |
970 |
KOEF. TOPLOTNE PROVODTI |
|
W/mK |
0,29 |
0,29 |
0,29 |
0,34 |
0,31 |
0,36 |
0,22 |
0,23 |
KOEF LINEAR. TOPLOT. ŠIRENJA |
α |
10-6/K |
85 |
85 |
150 |
120 |
190 |
150 |
160 |
|
HIGRO SKOPNOST |
% |
3 |
< 3 |
0,3 |
0 |
~ 0,3 |
0 |
0 |
0 |
|
ZAPALJIVOST |
gori |
gori |
gori |
gori |
gori |
gori |
gori |
ne gori |
||
ELEKTRICNE OSOBINE |
||||||||||
DIELEKTRICNA KONSTANTA +105HZ |
– DIN 53483 |
ε |
3,6 |
3,6 |
3,7-6 |
5 |
4 |
2,3 |
2,2-2,4 |
2,1 |
VDE 0303TEIL + 4/10×55 |
ε |
6-7 |
5,0 |
3,7-6 |
5 |
4 |
2,3 |
2,2-2,4 |
2,1 |
|
DIELEKT. FAKTOR GUBITKA KOD +105HZ |
– DIN 53483 |
0,02-0,03 |
0,026 |
0,21 |
0,0035 |
0,0002 |
0,0006 |
0,3-0,7 x 10-4 |
||
VDE 0303TEIL + 4/10×55 |
0,1-0,3 |
0,2 |
0,21 |
0,0035 |
0,0002 |
0,0006 |
||||
PROBOJNA CVRSTOCA |
– DIN 53481 |
kV/mm |
50 |
20 |
31 |
65-70 |
90 |
30-90 |
20-80 |
|
VDE 0303TEIL + 2/10×55 |
kV/mm |
20 |
20 |
65-70 |
90 |
30-90 |
20-80 |
|||
SPECIFICNI OTPOR NA PROBOJ |
– DIN 53482 |
Ω cm |
1015 |
1013 |
>1018 |
1018 |
||||
VDE 0303TEIL + 3/10×55 |
Ω cm |
1011 |
1013 |
1015 |
>1018 |
1016 – 1018 |
1018 |
|||
POVRŠINSKI OTPOR |
– DIN 53482 |
Ω |
1012 |
4,3 x 1013 |
108 |
>1013 |
1017 |
|||
VDE 0303TEIL + 3/10×55 |
Ω |
1010 |
4,3 x 1013 |
1013 |
>1018 |
5×1013 |
1017 |
|||
OTPOR LUTAJUCOJ STRUJI |
– DIN 53480 |
KA3c(T4) |
KA3c |
KA3c |
KA3c |
KA3c |
KA3c |
|||
VDE 0303TEIL + 1/9×64 |
KA3b(T4) |
KA3b |
KA3b |
KA3c |
KA3c |
Legenda:
– materijal suv
+ materijal kondicioniran
TERMOPLAST MATERIJALI HEMIJSKA POSTOJANOST |
|||||||||
1 | 2 | 3 | 4 | 5 | 6 | 7 | |||
REAGENS | KONCENTRACIJA % |
C° | PA 6 | PA 6 +G | PA 6 +
MOS2 |
L POM | PP | PE | PVDF |
aceton | 100 | 20 | + | + | + | + | – | ± | |
aluminujm hlorid |
10 | + | + | + | + | + | |||
amonijak (vodeni) |
100 | 20 | + | + | + | + | |||
80 | |||||||||
amonijska voda | 20 | + | + | + | |||||
80 | – | – | |||||||
benzaldehid | 0,1 | 20 | ± | + | ± | – | – | + | |
60 | ± | ± | – | – | + | ||||
benzin | 100 | 20 | + | + | + | + | ± | + | + |
60 | + | + | + | – | ± | ||||
benzol | 100 | 20 | + | + | + | + | ± | – | + |
60 | + | + | – | – | |||||
benzin-benzol smesa |
80/20 | 20 | + | + | – | – | |||
borna kiselina | razredjena | 40 | – | + | – | + | + | + | |
brom (vodeni) | 100 | 20 | – | – | + | ||||
butan (plin) | 50 | 20 | + | + | + | – | + | ||
cink hlorid | razredjena | 40 | ± | ± | ± | + | + | + | |
dekstrin (vodeni) |
zasicen | 20 | + | + | + | ||||
dikloretilen | 20 | ± | – | + | |||||
dizel ulje | 100 | 20 | + | + | + | + | + | + | |
100 | 60 | + | + | ± | ± | ||||
azotna kiselina |
do 30 | 40 | – | – | – | ± | ± | ± | + |
etilacetat | 100 | 20 | + | + | + | ± | ± | ± | |
etilalkohol | 96 | 20 | ± | + | ± | + | + | ||
fenol | 100 | 20 | – | – | – | – | + | + | |
flor (vodeni) | 100 | 20 | – | – | – | ||||
florovodicna kiselina |
do 40 | 20 | – | – | – | + | + | + | |
formaldehid | 40 | 20 | + | ± | + | + | + | + | + |
fotoemulzija | svaka | 40 | + | + | + | ||||
fotorazvijac | 40 | + | + | + | |||||
fotofiksir | 40 | + | + | + | |||||
fosfatna kiselina |
do 30 | 40 | – | ± | – | + | + | + | |
glukoza (vodena) |
zasicen | 20 | + | + | + | ||||
glikol (vodeni) |
60 | ± | + | + | + | + | + | + | |
glicerin (vodeni) |
svaka | 60 | + | + | + | + | + | + | |
hesan | 20 | + | + | + | + | + | + | ||
heptan | 20 | + | + | + | ± | – | + | ||
izooktan | 20 | + | + | + | + | + | + | ||
izopropilalkohol | 20 | ± | ± | ± | + | + | + | ||
jodtinktura | 20 | – | – | – | + | – | |||
kalcijumhlorid (vodeni) |
10 | 40 | + | + | + | + | + | + | |
kalcijumnitrat | 50 | 40 | + | + | |||||
hlor (plinovit) suv |
100 | 20 | – | – | + | – | |||
hlor (plinovit) vlazan |
5 | 20 | – | – | – | – | – | + | |
hloroform | teh.cist | 20 | – | – | – | ± | ± | – | + |
hromna kiselina |
50 | 20 | – | – | – | – | + | ± | + |
kalijum-bikromat | 40 | 20 | ± | ± | ± | + | + | + | |
kaljumhlorid | razredjena | 60 | + | + | + | ||||
kalijumnitrat | razredjena | 40 | + | + | + | + | + | ||
kalijumpremanganat | do 6 | 20 | ± | – | ± | + | + | + | + |
krezol | do 90 | 20 | ± | ± | + | + | + | ||
ksilol | 100 | 20 | + | + | + | + | + | ± | |
maslacna kiselina |
20 | 20 | – | – | + | + | + | + | |
magnezijumhlorid | razredjena | 40 | + | + | + | + | + | ||
maleinska kiselina |
zasicen | 40 | + | + | + | ||||
morska voda | 40 | + | + | + | + | + | + | ||
metilni alkohol |
100 | 40 | + | ± | + | + | + | + | + |
metiletilketon | 100 | 20 | + | + | + | ± | ± | + | ± |
mlecna kiselina |
10 | 20 | + | + | + | + | + | + | + |
mravlja kiselina |
85 | • | – | • | |||||
mineralno ulje | bez dodataka |
20 | + | + | + | + | + | + | + |
natrijum-karbonat | razredjena | 40 | + | + | + | + | + | + | + |
natrijum-hidroksid | do 40 | 40 | + | + | + | + | + | ||
natrijum-hlorid | razredjena | 40 | + | + | + | + | + | + | + |
natrijum-nitrat | zasicen | 60 | + | + | + | + | + | + | |
natrijum-sulfat | zasicen | 40 | + | + | + | + | |||
nitrobenzol | 20 | ± | ± | ± | + | + | + | ||
oleum | 10 | 20 | • | • | • | – | – | – | |
ozon | 2(vol) | 20 | ± | ± | ± | ± | ± | + | |
octena kiselina |
25-60 | 60 | – | ± | – | + | + | + | |
petroleter | teh.cist | 20 | + | + | + | + | + | + | |
pikrinska kiselina |
1 | 20 | + | + | + | ||||
piridin | 100 | 20 | + | + | + | + | + | ||
rezorcin | • | • | |||||||
solna kiselna | do 30 | 20 | ± | – | ± | – | + | + | + |
sumpor | 20 | + | ± | + | + | + | |||
sumpor-dioksid suv |
svaka | 20 | + | + | + | ||||
sumporna kiselina |
do 40 | 20 | ± | ± | – | + | + | + | |
96 | 20 | • | + | • | ± | – | + | ||
srebreni nitrat |
do 8 | 40 | + | + | + | + | + | ||
tetrahloretilen | 20 | ± | ± | ||||||
trihloretilen | 100 | 20 | ± | + | ± | ± | – | – | + |
tetrahlorugljenik | 100 | 20 | + | ± | + | + | – | – | + |
tetrahidrofuran | 100 | 20 | + | + | + | ± | – | ± | + |
toluol | 100 | 20 | + | + | + | + | + | + | |
ugljicni dioksid |
100 | 60 | + | + | + | ||||
ugljicna kiselina |
100 | 60 | + | + | + | ||||
vodokov peroksid |
do 30 | 20 | ± | ± | + | + | + | + | |
, + postojan ,. – nepostojan, ± uslovno postojan., • topiv |
|||||||||